不同添加剂对聚丙烯降解的影响

赵旭, 刘鑫, 吴昆鹏, 孔磊, 谭志勇

PDF(1502 KB)
PDF(1502 KB)
塑料科技 ›› 2024, Vol. 52 ›› Issue (04) : 104-108. DOI: 10.15925/j.cnki.issn1005-3360.2024.04.021
助剂

不同添加剂对聚丙烯降解的影响

作者信息 +

Effect of Different Additives on Polypropylene Degradation

Author information +
History +

摘要

文章以过氧化二叔丁基(DTBP)作为聚丙烯(PP)降解的引发剂,选择硬脂酸钴和硬脂酸锌作为催化过氧化物分解的添加剂,讨论添加剂对PP降解的影响。结果表明:随着DTBP含量的增加,PP的熔体流动速率(MFR)明显增加,力学性能下降,结晶性能提高。当引发剂含量增加到0.6%~0.8%时,熔融曲线出现双峰,黏度和模量下降。加入添加剂硬脂酸钴时,冲击性能下降34.63%,黏度和模量下降,PP的MFR进一步增加,最高的MFR比没有加入添加剂的样品高出59.08%,结晶性能高于没加添加剂的样品,晶体排列更规整。加入添加剂硬脂酸锌时,冲击性能下降,黏度和模量下降,最高的MFR比没有加入添加剂的样品高200.99%,晶体排列最规整。因此,硬脂酸锌更适合作为化学法降解PP的添加剂。

Abstract

Di-tert-butyl peroxide (DTBP) was used as the initiator of polypropylene (PP) degradation, and cobalt stearate and zinc stearate were selected as the additives to catalyze the decomposition of peroxide. The effects of additives on PP degradation was discussed. The results show that with the increase of DTBP content, the melt flow rate (MFR) of PP increases obviously, the mechanical properties decreases, and the crystallization properties improves. When the initiator content increases to 0.6%~0.8%, the melting curve shows two peaks, and the viscosity and modulus decreases. When cobalt stearate is added, the impact property is decreased by 34.63%, the viscosity and modulus decreases, and the MFR of PP further increases. The highest MFR is 59.08% higher than that of the sample without additive, and the crystallization property is higher than that of the sample without additive, and the crystal arrangement is more regular. When zinc stearate is added, the impact property decreases, and the viscosity and modulus decrease. The highest MFR is 200.99% higher than that of the sample without additive, and the crystal arrangement is the most regular. Therefore, zinc stearate is more suitable as an additive for chemical degradation of PP.

关键词

聚丙烯 / 过氧化二叔丁基 / 熔体流动速率 / 添加剂

Key words

Polypropylene / Di-tert-butyl peroxide / Melt flow rate / Additive

中图分类号

TQ325.1+4

引用本文

导出引用
赵旭 , 刘鑫 , 吴昆鹏 , . 不同添加剂对聚丙烯降解的影响. 塑料科技. 2024, 52(04): 104-108 https://doi.org/10.15925/j.cnki.issn1005-3360.2024.04.021
ZHAO Xu, LIU Xin, WU Kun-peng, et al. Effect of Different Additives on Polypropylene Degradation[J]. Plastics Science and Technology. 2024, 52(04): 104-108 https://doi.org/10.15925/j.cnki.issn1005-3360.2024.04.021

参考文献

1
李栋,艾纯金,张定军,等.聚丙烯熔喷布抗菌性能研究进展[J].塑料科技,2022,50(8):114-118.
2
XIAO Y, SAKIB N, YUE Z, et al. Study on the relationship between structure parameters and filtration performance of polypropylene melt-blown nonwovens[J]. Autex Research Journal, 2020, 20(4): 366-371.
3
李振军.聚丙烯熔喷法非织造布发展现状(下)[J].橡塑技术与装备,2020,46(22):25-30.
4
TZOGANAKIS C, TANG Y, VLACHOPOULOS J, et al. Controlled degradation of poly-propylene: A comprehensive experimental and theoretical investigation[J]. Polymer-Plastics Technology and Engineering, 1989, 28(3): 319-350.
5
AZIZI H, GHASEMI I, KARRABI M. Controlled-peroxide degradation of polypropylene: Rheological properties and prediction of MWD from rheological data[J]. Polymer Testing, 2008, 27(5): 548-554.
6
文渊,陈良鹏,李海波,等.可控流变聚丙烯的制备及性能研究[J].塑料工业,2021,49(2):36-39.
7
AZIZI H, GHASEMI I, KARRABI M. Controlled-peroxide degradation of polypropylene: Rheological properties and prediction of MWD from rheological data[J]. Polymer Testing, 2008, 27(5): 548-554.
8
杨锦,柳丽楠,金坤,等.降解法制备高流动性聚丙烯的研究[J].塑料工业,2022,50(4):90-93, 161.
9
方丽莉,李永贵,麻文效.化学降解法生产熔喷无纺布用聚丙烯专用料的研究[J].化工新型材料,2021,49(12):141-145.
10
KANG J, WANG B, PENG H, et al. Investigation on the structure and crystallization behavior of controlled-rheology polypropylene with different stereo-defect distribution[J]. Polymer Bulletin, 2014, 71: 563-579.
11
MA Z, MAHMUDOV K T, ALIYEVA V A, et al. Peroxides in metal complex catalysis[J]. Coordination Chemistry Reviews, 2021, DOI: 10.1016/j.ccr.2021.213859.
12
SHENG B R, LI B, XIE B H, et al. Influences of molecular weight and crystalline structure on fracture behavior of controlled-rheology-polypropylene prepared by reactive extrusion[J]. Polymer Degradation and Stability, 2008, 93(1): 225-232.
13
朱新远,田国华,王国明,等.规聚丙烯DSC熔融双峰的成因[J].高分子材料科学与工程,2001(1):75-78.
14
SPICKER C, RUDOLPH N, KÜHNERT I, et al. The use of rheological behavior to monitor the processing and service life properties of recycled polypropylene[J]. Food Packaging and Shelf Life, 2019, 19: 174-183.

基金

吉林省发改委产业化项目(2021C036-6)

评论

PDF(1502 KB)

Accesses

Citation

Detail

段落导航
相关文章

/