一步成型法制脂塑木复合板材工艺探究
胡建东, 殷晓飞, 吴丹, 黄莹辰, 曾浩宇, 林伟
一步成型法制脂塑木复合板材工艺探究
Process Exploration of Fat-plastic-wood Composite Panels by One-step Forming Method
研究旨在开发一步成型法制备脂塑木复合板材的工艺。以废弃印刷线路板(WPCB)为原料,通过非金属筛分、物料混合、挤出成型等工艺,制备脂塑木复合型材。中试最佳的物料配方为粒径0.125~0.150 mm的非金属粉235 kg、高密度聚乙烯(HDPE)新料105.0 kg、HDPE回收料157.5 kg、木粉465 kg、马来酸酐接枝聚乙烯63 kg和二元羧酸脂肪醇酯20 kg;混合后通过挤出机机筒加热、螺杆剪切得到热熔物料,热熔物料经合流芯进入模具挤出成型,最后经切割、冷却定型24 h,得到型材,测定其性能。中试生产板材最佳最小集中载荷保持在3 100 N以上,弯曲模量大于3 700 MPa,吸水率小于1%。研究为回收废弃印刷线路板非金属组分资源化利用提供了简单高效方法,在处理废弃印刷线路板非金属组分的同时产生经济效益,实现对废弃印刷线路板非金属组分的资源化利用。
The study aims to develop a one-step forming method for preparing wood-plastic composite boards. Using waste printed circuit boards (WPCB) as raw materials, wood-plastic composite profiles are prepared through processes such as non-metal screening, material mixing, and extrusion molding. The best material formulation for the pilot test was 235 kg of non-metallic powder with particle size of 0.125~0.150 mm, 105.0 kg of new HDPE, 157.5 kg of recycled HDPE, 465 kg of wood flour, 63 kg of maleic anhydride grafted polyethylene, and 20 kg of dibasic carboxylic acid fatty alcohol ester. After mixing, the hot-melt material was obtained by extruder barrel heating and screw shearing, and the hot-melt material entered into the mould for extrusion moulding through the merging core. Finally, the profile was obtained by cutting, cooling and shaping for 24 h, and its properties were determined. The optimum minimum concentrated load of the pilot-produced panel was kept above 3 100 N, the bending modulus was more than 3 700 MPa, and the water absorption rate was less than 1%. The research in this paper provides a simple and efficient method for recycling the non-metallic components of WPCB for resource utilization, and generates economic benefits while processing the non-metallic components of WPCB, and realizes the resource utilization of the non-metallic components of WPCB.
废弃印刷线路板 / 非金属粉 / 一步成型 / 复合板材 / 资源化利用
Waste printed circuit board / Non-metallic powder / One-step forming / Composite panels / Resource utilization
X799
1 |
薛建森,卫晓岚,邵志恒,等.国内废弃电子线路板处置技术研究与展望[J].再生资源与循环经济,2023,16(7):22-25.
|
2 |
|
3 |
|
4 |
王小雷,贺军.探讨电子垃圾污染的处置与管理[J].环境科学与管理,2006(2):19-21.
|
5 |
温雪峰,李金惠,朱雪梅,等.我国废弃电路板资源化现状及其对策[J].矿冶,2005(1):66-69.
|
6 |
|
7 |
|
8 |
|
9 |
马小垒.废弃线路板资源化利用研究[J].能源与节能,2021(7):187-190.
|
10 |
陈志燕.废弃印刷线路板的资源化回收技术分析[J].科技风,2017(25):122.
|
11 |
唐德文,邹树梁,刘衣昌,等.废弃电路板回收技术与方法研究进展[J].南华大学学报:自然科学版,2014,28(1):46-53, 58.
|
12 |
吴丹,殷晓飞,李智,等.废线路板非金属材料资源化再生技术现状[J].广东化工,2023,50(2):116-117
|
13 |
|
14 |
|
15 |
|
16 |
|
17 |
叶子玮,代银娟,李航,等.热解法在废线路板处理处置中的应用研究进展[J].云南化工,2024,51(2):15-18.
|
18 |
|
19 |
|
20 |
|
21 |
|
22 |
王祖润,杜中,张永贵,等.废弃线路板非金属残渣作填充料对镁质胶凝材料性能的影响[J].混凝土与水泥制品,2017(8):87-90.
|
23 |
郭光辉,张恩源,刘清.掺废线路板非金属材料的水泥稳定碎石路用性能试验研究[J].武汉理工大学学报:交通科学与工程版,1-12[2024-06-08].
|
24 |
徐丽军,关杰,袁昊,等.掺杂废弃线路板非金属粉末的粉刷石膏复合材料的力学性能[J].环境工程学报,2017,11(4):2439-2446.
|
25 |
雷文,余旺旺,任超.几种木塑复合材料的性能对比[J].塑料科技,2008,36(3):40-45.
|
26 |
郑景新,庞浩,陈永,等.反应挤出制备HDPE-HD/甘蔗渣木塑复合材料[J].塑料工业,2008,22(2):57-61.
|
27 |
薛敏.相容剂在木塑复合材料中的应用研究现状[J].塑料科技,2009,37(1):87-90.
|
28 |
陈鸿景.废旧塑料再生造粒工艺浅析[J].皮革制作与环保科技,2023,4(9):92-93, 99.
|
29 |
吕柏灿.废旧塑料再生造粒工艺研究[J].设备管理与维修,2018(8):142-143.
|
30 |
黄兴元,乐建晶,柳和生,等.废旧塑料再生造粒工艺浅析[J].工程塑料应用,2015,43(4):134-138.
|
/
〈 |
|
〉 |