焦磷酸哌嗪复配阻燃剂在聚丙烯中阻燃性能的研究

作者信息 +

Study on Flame Retardancy of Piperazine Pyrophosphate Compound Flame Retardant in Polypropylene

Author information +
History +

摘要

将焦磷酸哌嗪(PPAP)分别与多种阻燃剂进行复配以制备膨胀型阻燃剂(IFR),最后与聚丙烯(PP)共混制备PP阻燃复合材料。采用垂直燃烧、极限氧指数(LOI)、锥形量热、热重分析和力学性能等测试手段对这几种复合材料进行表征。结果表明:与PP样品相比,复合材料的LOI由17.6%升至26%以上,残炭率由0.09%增加至1.98%以上,热分解T 1%T 5%分别升高11.4 ℃和41.2 ℃以上,说明阻燃剂的加入增强了阻燃性能。同时,复合材料的热释放速率峰值、平均热释放量、总热释放量、总产烟量大幅降低,阻燃及抑烟性能明显提升,而力学性能反而降低。获得PPAP与三聚氰胺焦磷酸盐(DMPY)复配的阻燃效果最佳,其中LOI为29.2%,残炭率为2.65%,热分解T 1%T 5%分别为286.6 ℃和372.7 ℃,且力学性能受影响最小。

Abstract

Piperazine pyrophosphate (PPAP) was compounded with a variety of flame retardants to prepare intumescent flame retardant (IFR), and finally blended with polypropylene (PP) to prepare PP flame retardant composites. These composites were characterized by vertical combustion, limiting oxygen index (LOI), cone calorimetry, thermogravimetric analysis and mechanical properties. The results show that compared with PP samples, the LOI of these composites increases from 17.6% to more than 26%, the carbon residue rate increases from 0.09% to more than 1.98%, and the thermal decomposition T 1% and T 5% increase by 11.4 ℃ and 41.2 ℃, respectively, indicating that the addition of flame retardant enhanced the flame retardant. At the same time, the peak heat release rate, average heat release, total heat release and total smoke production of these composites are greatly reduced, and the flame retardancy and smoke suppression properties are significantly improved, while the mechanical properties are reduced. The flame retardant effect of PPAP and melamine pyrophosphate (DMPY) is the best, in which the LOI is 29.2%, the carbon residue rate is 2.65%, the thermal decomposition T 1% and T 5% are 286.6 °C and 372.7 °C, respectively, and the mechanical properties are the least affected.

关键词

焦磷酸哌嗪 / 膨胀型阻燃剂 / 聚丙烯 / 阻燃性能

Key words

Piperazine pyrophosphate / Intumescent flame retardant / Polypropylene / Flame retardancy

中图分类号

TQ325.1+4 / TB332

引用本文

导出引用
陆忠海 , 杨晓龙 , 龙德晓 , . 焦磷酸哌嗪复配阻燃剂在聚丙烯中阻燃性能的研究. 塑料科技. 2024, 52(05): 52-57 https://doi.org/10.15925/j.cnki.issn1005-3360.2024.05.011
LU Zhong-hai, YANG Xiao-long, LONG De-xiao, et al. Study on Flame Retardancy of Piperazine Pyrophosphate Compound Flame Retardant in Polypropylene[J]. Plastics Science and Technology. 2024, 52(05): 52-57 https://doi.org/10.15925/j.cnki.issn1005-3360.2024.05.011

参考文献

1
杨帅,宋雨方,钟炜锋,等.自成膜聚丙烯酸酯胶体的制备及其性能研究[J].辽宁石油化工大学学报,2023,43(3):1-7.
2
CHEN C, SU S Q, SUN M M, et al. Synergistic flame retardancy of ZnO with piperazine pyrophosphate/melamine polyphosphate in PP[J]. Polymer Testing, 2023, DOI: 10.1016/j.polymertesting.2022.107878.
3
FERNÁNDEZ A, SANTANGELO-MURO M, FERNÁNDEZ-BLÁZQUEZ J P, et al. Processing and properties of long recycled-carbon-fibre reinforced polypropylene[J]. Composites Part B Engineering, 2021, DOI: 10.1016/j.compositesb.2021.108653.
4
LI W X, ZHANG H J, HU X P, et al. Highly efficient replacement of traditional intumescent flame retardants in polypropylene by manganese ions doped melamine phytate nanosheets[J]. Journal of Hazardous Materials, 2020, DOI: 10.1016/j.jhazmat.2020.123001.
5
ZHANG N E, ZHANG J, YAN H, et al. A novel organic-inorganic hybrid K-HBPE@APP performing excellent flame retardancy and smoke suppression for polypropylene[J]. Journal of Hazardous Materials, 2019, 373: 856-865.
6
TAO M, QIAN L, WANG J, et al. From physical mixtures to block copolymer: Impose outstandingly toughening and flame retardant effect to polypropylene[J]. Composites, PartB. Engineering, 2023, DOI: 10.1016/j.compositesb.2023.110538.
7
ZHOU Y, HE W, WU Y, et al. Influence of thermo-oxidative aging on flame retardancy, thermal stability, and mechanical properties of long glass fiber-reinforced polypropylene composites filled with organic montmorillonite and intumescent flame retardant[J]. Journal of Fire Sciences, 2019, 37(2): 176-189.
8
XIAO X, HU S, ZHAI J G, et al. Thermal properties and combustion behaviors of flame-retarded glass fiber-reinforced polyamide 6 with piperazine pyrophosphate and aluminum hypophosphite[J]. Journal of Thermal Analysis and Calorimetry, 2016, 125(1): 175-185.
9
杜玉莹.焦磷酸哌嗪基膨胀型阻燃剂对聚烯烃的阻燃作用研究[D].青岛:青岛科技大学,2019.
10
LEE S J, MORGAN A B, SCHIRALDI D A, et al. Improving the flame retardancy of polypropylene foam with piperazine pyrophosphate via multilayering coextrusion of film/foam composites[J]. Journal of Applied Polymer Science, 2020, DOI: 10.1002/app.48552.
11
ZHU P B, XU M J, LI S, et al. Preparation and investigation of efficient flame retardant TPE composites with piperazine pyrophosphate/aluminum diethylphosphinate system[J]. Journal of Applied Polymer Science, 2019, DOI: 10.1002/APP.47711.
12
LIU L B, XU Y, HE Y T, et al. A facile strategy for enhancing the fire safety of unsaturated polyester resins through introducing an efficient mono-component intumescent flame retardant[J]. Polymers for Advanced Technologies, 2020, 31(6): 1218-1230.
13
XIAO X, ZHAI J G, CHEN T, et al. Flame retardant properties of polyamide 6 with piperazine pyrophosphate[J]. Plastics Rubber and Composites, 2017, 46(5): 193-199.
14
ZHAO P P, GUO C G, LI L P. Flame retardancy and thermal degradation properties of polypropylene/wood flour composite modified with aluminum hypophosphite/melamine cyanurate[J]. Springer International Publishing, 2019, 135(6): 3085-3093.
15
LI S S, LIU Y, LIU Y S, et al. Synergistic effect of piperazine pyrophosphate and epoxy-octavinyl silsesquioxane on flame retardancy and mechanical properties of epoxy resin[J]. Composites Part B: Engineering, 2021, DOI: 10.1016/j.compositesb.2021.109115.
16
HU Z, ZHONG Q Z, GONG X D. Flame retardancy, thermal properties, and combustion behaviors of intumescent flame-retardant polypropylene containing (poly) piperazine pyrophosphate and melamine polyphosphate[J]. Polymers for Advanced Technologies, 2020, 31(11): 2701-2710.
17
张振环,马航,万邦隆,等.焦磷酸哌嗪的制备及其在高分子材料阻燃中的应用[J].磷肥与复肥,2022,37(5):16-18.
18
马殿普,郎丽君,潘飞,等.焦磷酸哌嗪协同次磷酸铝阻燃聚丙烯复合材料性能[J].工程塑料应用,2023,51(4):133-138.
19
ZHU C J, HE M S, LIU Y, et al. Synthesis and application of a mono-component intumescent flame retardant for polypropylene[J]. Polymer Degradation and Stability, 2018, 151: 144-151.
20
张炎,林凤龙,吴银财,等.焦磷酸哌嗪/聚磷酸铵对硅灰石增强聚丙烯的阻燃应用研究[J].塑料工业,2022,50(5):177-206.
21
杨晓龙,刘晨曦,李云东,等.磷酸硼协效膨胀型阻燃剂对聚丙烯阻燃性能的研究[J].塑料科技,2022,50(8):72-76.
22
JIAO Y H, WANG X L, WANG Y Z, et al. Thermal degradation and combustion behaviors of flame-retardant polypropylene/thermoplastic polyurethane blends[J]. Journal of Macromolecular Science, Part B, 2009, 48(5): 889-909.
23
苏淑倩.焦磷酸哌嗪的合成及对聚丙烯的阻燃作用研究[D].青岛:青岛科技大学,2022.
24
李永翔,尹思浩,谢于辉,等.纳米黑磷阻燃聚丙烯及对力学性能的影响[J].复合材料学报,2022,39(7):3178-3190.
25
刘洋.焦磷酸哌嗪的制备及在阻燃聚丙烯中的应用[D].沈阳:沈阳工业大学,2022.
26
LI S S, LIU Y, LIU Y S, et al. Synergistic effect of piperazine pyrophosphate and epoxy-octavinyl silsesquioxane on flame retardancy and mechanical properties of epoxy resin[J]. Composites Part B: Engineering, 2021, DOI: 10.1016/j.compositesb.2021.109115.
27
乔金莲.新型成炭剂的合成及其在阻燃聚丙烯材料中的应用研究[J].塑料科技,2021,49(10):46-50.
28
XIAO X, ZHAI J G, CHEN T, et al. Flame retardant properties of polyamide 6 with piperazine pyrophosphate[J]. Plastics, Rubber and Composites, 2017, 46(45): 193-199.
29
YUAN Z, WEN H, LIU Y, et al. Synergistic effect between piperazine pyrophosphate and melamine polyphosphate in flame retarded glass fiber reinforced polypropylene[J]. Polymer Degradation and Stability, 2021, DOI: 10.1016/j.polymdegradstab.2020.109477.
30
NI J X, TAI Q L, LU H D, et al. Microencapsulated ammonium polyphosphate with polyurethane shell: Preparation, characterization, and its flame retardance in polyurethane[J]. Polymers for Advanced Technologies, 2010, 21(6): 392-400.
31
HANG Z, RUAN B, WU J, et al. High-efficiency ammonium polyphosphate intumescent encapsulated polypropylene flame retardant[J]. Journal of Applied Polymer Science, 2016, 138(20): 58-67.
32
PAN Y T, LUO Z L, WANG B B. Synergistic flame retardant effect of piperazine salt and ammonium polyphosphate as intumescent flame retardant system for polypropylene[J]. Journal of Applied Polymer Science, 2021, DOI: 10.1002/app.49813.

评论

PDF(1662 KB)

Accesses

Citation

Detail

段落导航
相关文章

/