Preparation and Properties of Mixed Starch/Polyvinyl Alcohol Composite Film
CHENG Wen-xi, MIAO Wei, BAI Shen-ao, SONG Wei-qiang, CAO Yuan-hang, WANG Hong-sen, AN Shun-li
Preparation and Properties of Mixed Starch/Polyvinyl Alcohol Composite Film
Dual mixed starch/polyvinyl alcohol (PVA) composite films were prepared by solution casting, in which corn starch, oxidized starch, and esterified starch were used as raw materials, glycerol and PVA as mix plasticizer, their appearances and transmittances were tested, and it was found that the mixed starch/PVA composite film with equal weight of corn starch and oxidized starch had good brightness, with the highest transmittance under ultraviolet, infrared, and visible light. The effect of corn starch content in mixed starch on the composite films were further investigated. The results showed that the mixed starch/PVA composite films had high light transmittance, and the visible light transmittance was higher than 55%. When the corn starch content is 30%, the mixed starch/PVA composite film has the highest tensile strength of 17.5 MPa. The moisture absorption rate of all starch/PVA composite films reached the equilibrium absorption rate after 40 h, and the mixed starch/PVA composite film with 30% corn starch content had the highest moisture absorption rate of 48.9%. Overall, the mixed starch/PVA composite film with 30% corn starch content had the best performance.
Starch/PVA composite film / Plasticization / Solution casting / Transparency / Mechanical properties
1 |
高哈尔·努拉里.可降解塑料的发展现状及其应用研究进展[J].合成材料老化与应用,2022,51(4):127-129..
|
2 |
|
3 |
吴张永,陆冲,程树军,等.淀粉基生物降解塑料[J].塑料科技,2003(1):59-64.
|
4 |
|
5 |
|
6 |
|
7 |
|
8 |
|
9 |
|
10 |
|
11 |
周剑敏,卢玥,汤晓智.淀粉-层状硅酸盐黏土复合薄膜的结构与性能研究[J].中国粮油学报,2017,32(12):50-55.
|
12 |
李凤红,吴全才,赵文凯,等.高淀粉含量玉米淀粉膜的制备及结构性能研究[J].现代化工,2009,29(12):43-45, 47.
|
13 |
|
14 |
|
15 |
陈卓,宋俏微,张水洞,等.氧化淀粉的抑菌效果及草莓涂膜保鲜应用[J].食品科学,2022,43(21):324-331.
|
16 |
|
17 |
彭雅丽,彭思敏,周全军,等.酸解酯化复合变性淀粉制备可食淀粉膜工艺研究[J].食品工程,2022,165(4):48-54.
|
18 |
王鑫.纳米银-氧化淀粉涂膜对无籽露葡萄和南丰蜜桔的保鲜性及安全性探究[D].北京:北京林业大学,2020.
|
19 |
|
20 |
孙复钱,王小玉,胡银,等.聚乙烯醇/氧化淀粉/二氧化钛复合纳米纤维膜的制备[J].高分子材料科学与工程,2016,32(2):155-159.
|
21 |
|
22 |
盛繁.氧化淀粉改性聚乙烯醇建筑胶黏剂的制备及最优参数选取[J].中国胶粘剂,2020,29(10):15-19.
|
23 |
王存堂,李子钰,林新,等.玉米淀粉/卡拉胶/甘油复合膜的最佳成膜工艺研究[J].食品安全质量检测学报,2022,13(3):799-804.
|
24 |
高奇奇,郝艳玲,程龙,等.玉米淀粉/TiO2纳米复合薄膜制备与性能[J].中国塑料,2023,37(2):45-50.
|
25 |
梅小虎,崔燕玲,杨水莲,等.变性淀粉聚乙烯醇复合膜的性能研究[J].食品安全导刊,2022(11):97-100.
|
26 |
李平,葛雪松,姜义军,等.马铃薯氧化淀粉的制备及其成膜性研究[J].粮食与油脂,2016,29(8):42-46.
|
27 |
董增,龙涛,张海静,等.纳米TiO2/氧化淀粉/PVA复合膜制备及其特性[J].塑料工业,2019,47(9):120-123, 128.
|
28 |
张静贤,龙柱,覃程荣,等.微晶纤维素/明胶对淀粉复合薄膜性能影响研究[J].功能材料,2022,53(12):12170-12176.
|
/
〈 |
|
〉 |