Preparation and Properties of Polyesters from Copolymerization of Cyclic Anhydrides and Epoxides
LI Si-xuan, LI Peng, DAI Xin, LI Xiao-shuang, HU Jun-hang, SONG Zhao-zheng, JIANG Qing-zhe
Preparation and Properties of Polyesters from Copolymerization of Cyclic Anhydrides and Epoxides
In order to solve the problems of high energy consumption of condensation polymerization and small variety of monomers for ring-opening polymerization of cyclic esters in the process of synthesizing polyesters, six polyester products were successfully synthesized using aminophenolic iron-based complexes to catalyze the copolymerization reaction of cyclic anhydride and epoxides. Nuclear magnetic resonance hydrogen spectroscopy (1H NMR), Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), contact angle meter, thermogravimetric analysis (TG), differential scanning calorimetry (DSC), and gel permeation chromatography (GPC) were used to characterize the structures and properties of polyester. The results showed that all the polyesters with hydrophilic properties were amorphous structures. The initial decomposition temperature (T 5%) of polyesters was 250~300 ℃ and the glass transition temperature (T g) of polyesters was 55~139 ℃. Polyesters containing rigid cyclohexane structure showed higher T g and better thermomechanical stability performance.
1 |
|
2 |
舒扬,熊兵,唐诗琪.含酰亚胺环聚硅氧烷的制备和热学性能研究[J].塑料科技,2023,51:68-71.
|
3 |
孔俊俊,陈传宗,卢晨晨,等.新型聚酯增塑聚乳酸材料的制备及性能研究[J].塑料科技,2021,49:1-5.
|
4 |
|
5 |
|
6 |
|
7 |
|
8 |
高传慧,汪曼秋,刘雪涵,等.衣康酸类水性自乳化聚酯合成及点击固化研究[J].辽宁石油化工大学学报,2020,40(4):41-48.
|
9 |
|
10 |
|
11 |
|
12 |
|
13 |
|
14 |
|
15 |
|
16 |
|
17 |
李帅,王昱博,季鹤源,等.(Salen)TiIVCl2配合物催化环氧化物和环酸酐开环交替共聚[J].高分子学报,2020,51:1039-1048.
|
18 |
|
19 |
|
20 |
|
21 |
|
22 |
|
23 |
|
24 |
|
25 |
|
26 |
|
27 |
|
28 |
乐天俊.结晶性含硫聚合物的精准合成[D].大连:大连理工大学,2020.
|
29 |
|
/
〈 |
|
〉 |