Effect of artificial aging on optical properties of ultra-translucent zirconia ceramics of different brands
Chen Luona, Zhang Xin, Tian Zhengyu, Wang Jian
PDF(1308 KB)
PDF(1308 KB)
Effect of artificial aging on optical properties of ultra-translucent zirconia ceramics of different brands
), Zhang Xin1, Tian Zhengyu2, Wang Jian1()Objective This work aimed to evaluate the effect of artificial aging on the translucency and color difference (ΔE) of ultra-translucent zirconia and provide a reference for clinical application. Methods The discs of ultra-translucent zirconia from six brands (Wieland, 3M ESPE, Amann Girrbach, Kuraray Noritake, Upcera, and Besmile) were cut and sintered according to each manufacturer’s product instructions; the experimental groups were named ZNT, LVP, AG, KAT, UPC, and BSM, respectively. IPS e.max Press was used as the control group (PLT). The specimens (n=6) were prepared with a diameter of 14 mm and a thickness of 1 mm. The specimens were subjected to artificial aging treatment according to the following conditions: in an autoclave at 134 ℃ at 0.2 MPa for 4, 8, and 12 h. According to the CIE1976Lab system, the CIE L*, a*, and b* values of the specimens before and after aging were measured by a co-lorimeter. The translucency parameter (TP) and ΔE were calculated. Results The mean TP values of each group before aging inorder were PLT>KAT>AG>ZNT>BSM>UPC>LVP. We found no significant difference in translucency in all experimental groups after aging for 4 and 8 h compared with those before aging. After 12 h of aging, the TP values of the KAT and ZNT groups were not significantly different from those before aging, but the TP values of the AG, BSM, LVP, and UPC groups were significantly lower than those before aging (P<0.05). The TP value of the control group was significantly higher than that of the other experimental groups at different stages (P<0.05). ΔE=3.3 was considered the visible color difference, and ΔE was less than 3.3 in all groups after 4 h of aging. After aging for 8 h, ΔE of the UPC group was slightly higher than 3.3. ΔE of the BSM and UPC groups was greater than 3.3 after 12 h of aging. Conclusion The TP and ΔE of different brands of ultra-translucent zirconia may change after various aging times. The translucency of some zirconia showed a decreasing trend and the color difference showed an increasing trend with the aging time.
zirconia / low-temperature degradation / optical property / translucency / color difference
R783.1
| 1 | Salah K, Sherif AH, Mandour MH, et al. Optical effect of rapid sintering protocols on different types of zirconia[J]. J Prosthet Dent, 2023, 130(2): 253.e1-253.e7. |
| 2 | Chevalier J, Gremillard L, Virkar AV, et al. The tetragonal-monoclinic transformation in zirconia: lessons lear-ned and future trends[J]. J Am Ceram Soc, 2009, 92(9): 1901-1920. |
| 3 | Chevalier J, Cales B, Drouin JM. Low-temperature a-ging of Y-TZP ceramics[J]. J Am Ceram Soc, 2004, 82(8): 2150-2154. |
| 4 | Khashayar G, Bain PA, Salari S, et al. Perceptibility and acceptability thresholds for colour differences in dentistry[J]. J Dent, 2014, 42(6): 637-644. |
| 5 | Paravina RD, Pérez MM, Ghinea R. Acceptability and perceptibility thresholds in dentistry: a comprehensive review of clinical and research applications[J]. J Esthet Restor Dent, 2019, 31(2): 103-112. |
| 6 | Bona A, Pecho O, Alessandretti R. Zirconia as a dental biomaterial[J]. Materials(Basel), 2015, 8(8): 4978-4991. |
| 7 | Zhang Y. Making yttria-stabilized tetragonal zirconia translucent[J]. Dent Mater, 2014, 30(10): 1195-1203. |
| 8 | 万乾炳. 口腔氧化锆修复材料分代之我见[J]. 国际口腔医学杂志, 2021, 48(2): 125-128. |
| 8 | Wan QB. My opinion on the generations of dental zirconia materials[J]. Int J Stomatol, 2021, 48(2): 125-128. |
| 9 | Jing Q, Zhang F, Lei L, et al. Improving low temperature degradation of 3Y-TZP ceramics via high tempe-rature carburizing[J]. Ceram Int, 2023, 49(8): 11865-11874. |
| 10 | Wu ZK, Li N, Yan JZ, et al. Effect of hydrothermal a-ging on the phase stability, microstructure and mechanical properties of dental 3Y-TZP ceramics[J]. Appl Mech Mater, 2014, 529: 251-255. |
| 11 | Walczak K, Mei?ner H, Range U, et al. Translucency of zirconia ceramics before and after artificial aging[J]. J Prosthodont, 2019, 28(1): e319-e324. |
| 12 | Porojan L, Vasiliu RD, B?rdeanu MI, et al. Surface cha-racterization and optical properties of reinforced dental glass-ceramics related to artificial aging[J]. Molecules, 2020, 25(15): 3407. |
| 13 | Pecho OE, Benetti P, Ruiz-López J, et al. Optical properties of dental zirconia, bovine dentin, and enamel-dentin structures[J]. J Esthet Restor Dent, 2024, 36(3): 511-519. |
| 14 | Kim HK, Kim SH. Effect of hydrothermal aging on the optical properties of precolored dental monolithic zirconia ceramics[J]. J Prosthet Dent, 2019, 121(4): 676-682. |
| 15 | Fathy SM, El-Fallal AA, El-Negoly SA, et al. Translucency of monolithic and core zirconia after hydrothermal aging[J]. Acta Biomater Odontol Scand, 2015, 1(2/3/4): 86-92. |
| 16 | Alghazzawi TF. The effect of extended aging on the optical properties of different zirconia materials[J]. J Prosthodont Res, 2017, 61(3): 305-314. |
| 17 | Miyazaki T, Nakamura T, Matsumura H, et al. Current status of zirconia restoration[J]. J Prosthodont Res, 2013, 57(4): 236-261. |
| 18 | Pereira GKR, Venturini AB, Silvestri T, et al. Low-temperature degradation of Y-TZP ceramics: a systematic review and meta-analysis[J]. J Mech Behav Biomed Mater, 2015, 55: 151-163. |
| 19 | Camposilvan E, Leone R, Gremillard L, et al. Aging resistance, mechanical properties and translucency of different yttria-stabilized zirconia ceramics for monolithic dental crown applications[J]. Dent Mater, 2018, 34(6): 879-890. |
| 20 | Pekkan G, Pekkan K, Bayindir B?, et al. Factors affecting the translucency of monolithic zirconia ceramics: a review from materials science perspective[J]. Dent Mater J, 2020, 39(1): 1-8. |
| 21 | Zhang F, Inokoshi M, Batuk M, et al. Strength, toughness and aging stability of highly-translucent Y-TZP ceramics for dental restorations[J]. Dent Mater, 2016, 32(12): e327-e337. |
| 22 | Sulaiman TA, Abdulmajeed AA, Donovan TE, et al. Optical properties and light irradiance of monolithic zirconia at variable thicknesses[J]. Dent Mater, 2015, 31(10): 1180-1187. |
| 23 | Tabatabaian F, Dalirani S, Namdari M. Effect of thickness of zirconia ceramic on its masking ability: an in vitro study[J]. J Prosthodont, 2019, 28(6): 666-671. |
/
| 〈 |
|
〉 |
AI Summary