Effect of speed sintering and aging on the translucency of high-translucent zirconia
Li Yan, Zhong Mengyi, Yang Ying
PDF(2152 KB)
PDF(2152 KB)
Effect of speed sintering and aging on the translucency of high-translucent zirconia
), Zhong Mengyi1,2,3, Yang Ying1,2,3()Objective This work aimed to evaluate the effect of speed sintering and low-temperature degradation on the translucency of high-translucent zirconia. Methods The ST and TT specimens were randomly divided into two groups depending on the sintering process: conventional sintering and speed sintering. The sintered specimens were divided into three subgroups according to the aging time: aged for 0, 5, and 20 h. Chromatic parameters (L*, a*, and b* values) were measured by Shade Eye NCC computer colorimeter in a dark environment under black and white background, and the translucency parameter (TP) was used to evaluate the translucency of zirconia. Results Speed sintering may decrease the TP of ST and increase the TP of TT. As for the effect of low-temperature degradation on the translucency of zirconia, the TP of ST decreased with the extension of aging time, and no significant difference was found in rapid sintering ST. Although the TP of TT decreased, no statistical difference was observed. Conclusion Speed sintering may decrease the translucency of high-strength zirconia and increase the translucency of high-translucent zirconia. Low-temperature degradation had no effect on the translucency of high-translucent zirconia. Speed sintering can be recommended for high-translucent zirconia in terms of translucency.
high-translucent zirconia / speed sintering / low-temperature degradation / translucency
R783.1
| 1 | 万乾炳. 口腔氧化锆修复材料分代之我见[J]. 国际口腔医学杂志, 2021, 48(2): 125-128. |
| 1 | Wan QB. My opinion on the generations of dental zirconia materials[J]. Int J Stomatol, 2021, 48(2): 125-128. |
| 2 | Johnston WM, Ma T, Kienle BH. Translucency parameter of colorants for maxillofacial prostheses[J]. Int J Pro-sthodont, 1995, 8(1): 79-86. |
| 3 | Kurtulmus-Yilmaz S, Ulusoy M. Comparison of the tran-slucency of shaded zirconia all-ceramic systems[J]. J Adv Prosthodont, 2014, 6(5): 415-422. |
| 4 | Lawson NC, Maharishi A. Strength and translucency of zirconia after high-speed sintering[J]. J Esthet Restor Dent, 2020, 32(2): 219-225. |
| 5 | Juntavee N, Attashu S. Effect of different sintering process on flexural strength of translucency monolithic zirconia[J]. J Clin Exp Dent, 2018, 10(8): e821-e830. |
| 6 | Zhang Y. Making yttria-stabilized tetragonal zirconia translucent[J]. Dent Mater, 2014, 30(10): 1195-1203. |
| 7 | Liu H, Inokoshi M, Nozaki K, et al. Influence of high-speed sintering protocols on translucency, mechanical properties, microstructure, crystallography, and low-temperature degradation of highly translucent zirconia[J]. Dent Mater, 2022, 38(2): 451-468. |
| 8 | ?oki? SM, Cóndor M, Vleugels J, et al. Mechanical properties-translucency-microstructure relationships in commercial monolayer and multilayer monolithic zirconia ceramics[J]. Dent Mater, 2022, 38(5): 797-810. |
| 9 | Ersoy NM, Aydo?du HM, De?irmenci Bü, et al. The effects of sintering temperature and duration on the flexu-ral strength and grain size of zirconia[J]. Acta Biomater Odontol Scand, 2015, 1(2/4): 43-50. |
| 10 | Hafezeqoran A, Sabanik P, Koodaryan R, et al. Effect of sintering speed, aging processes, and different surface treatments on the optical and surface properties of monolithic zirconia restorations[J]. J Prosthet Dent, 2023, 130(6): 917-926. |
| 11 | Zhang CY, Agingu C, Tsoi JKH, et al. Effects of aging on the color and translucency of monolithic translucent Y-TZP ceramics: a systematic review and meta-analysis of in vitro studies[J]. Biomed Res Int, 2021, 2021: 8875023. |
| 12 | Fathy SM, El-Fallal AA, El-Negoly SA, et al. Translucency of monolithic and core zirconia after hydrothermal aging[J]. Acta Biomater Odontol Scand, 2015, 1(2/4): 86-92. |
| 13 | Inokoshi M, Zhang F, De Munck J, et al. Influence of sintering conditions on low-temperature degradation of dental zirconia[J]. Dent Mater, 2014, 30(6): 669-678. |
| 14 | Kohorst P, Borchers L, Strempel J, et al. Low-temperature degradation of different zirconia ceramics for dental applications[J]. Acta Biomater, 2012, 8(3): 1213-1220. |
| 15 | Park MG. Effect of low-temperature degradation treatment on hardness, color, and translucency of single la-yers of multilayered zirconia[J]. J Prosthet Dent, 2023. doi: 10.1016/j.prosdent.2023.01.023 . |
| 16 | Zhang F, Inokoshi M, Batuk M, et al. Strength, toughness and aging stability of highly-translucent Y-TZP ceramics for dental restorations[J]. Dent Mater, 2016, 32(12): e327-e337. |
| 17 | Choi YS, Kang KH, Att W. Effect of aging process on some properties of conventional and multilayered translucent zirconia for monolithic restorations[J]. Ceram Int, 2020, 46(2): 1854-1868. |
| 18 | Jansen JU, Lümkemann N, Letz I, et al. Impact of high-speed sintering on translucency, phase content, grain sizes, and flexural strength of 3Y-TZP and 4Y-TZP zirconia materials[J]. J Prosthet Dent, 2019, 122(4): 396-403. |
| 19 | Attachoo S, Juntavee N. Role of sintered temperature and sintering time on spectral translucence of nano-crystal monolithic zirconia[J]. J Clin Exp Dent, 2019, 11(2): e146-e153. |
/
| 〈 |
|
〉 |
AI Summary